Product Name: Liner, high wear-resistant liner
Commonly used aliases: lining, partition board, raft, purlin, sieve, screen
Main material: Mn13, Mn13Cr2
Casting process: lost foam casting
Applicable materials: granite, basalt, etc.
Applications: Smelting, building materials, roads, railways, water conservancy and chemicals
The high wear-resistant lining plate developed and produced by Jiangsu Hudong Machinery Casting Co., Ltd. is the latest wear-resistant product developed by absorbing domestic and foreign advanced technology. The high-chromium alloy lining plate is combined with the latest industrial and mining conditions of domestic sand and gravel industry. A generation of crusher liners. The lining board adopts new manufacturing technology and unique structural design. The finished product is cubic, no tension and crack, and the granular shape is quite good. It can crush various coarse, medium and small, and the compressive strength does not exceed 350MPa. Fine materials (granite, limestone, concrete, etc.) are widely used in various ore crushing, railway, highway, energy, cement, chemical, construction and other industries. They are high wear-resistant lining castings that are trusted by major manufacturers.
British Weir custom liner
High manganese steel is divided into five grades according to national standards. The main difference is the carbon content, which ranges from 0.75% to 1.45%. It is subject to high impact and low carbon content. The commonly used high-manganese steel grades and their applicable range are: ZGMn13-1 (C 1.10%~1.50%) for low impact parts, ZGMn13-2 (C1.00%~1.40%) for ordinary parts, ZGMn13-3 (C0.90% to 1.30%) for complex parts, ZGMn13-4 (C0.90%~1.20%) for high impact parts. The manganese content of the above four grades of steel is 11.0% to 14.0%. The manganese content is between 11.0% and 14.0%, and generally should not be lower than 13%. Ultra-high manganese steel has no national standard, but the manganese content should be greater than 18%. The level of silicon is high, and chromium is used to improve wear resistance, generally around 2.0%. It is often used to make the shovel tooth of the excavator, the rolling wall and the crushing wall of the cone crusher, the jaw crusher jaw plate, the ball mill liner, the plate hammer, the hammer head, and the like.
Why choose us:
The three major system integration certification enterprises, Hudong Foundry passed the ISO9001 quality management system, CE certification, China Foundry Association members, Jiangsu AAA-level contract and keeping promises units.
Excellent manufacturing equipment such as medium frequency induction furnace, large natural gas heat treatment furnace and large-scale spray shot blasting machine have won the Chinese casting field.
The existing imported direct reading spectrometer, tensile testing machine, ultrasonic flaw detector and other advanced testing equipment, the implementation of strict inspection, size and appearance inspection of the factory products.